Can someone clarify the underfill and / or concavity parameter requested in that specification. What do they mean by individual defect - maximum depth of 0.07T or 0.030 in (whichever is less)?
That's a good question.You would think that if the discontinuity did not extend the full length of the weld,then it would be 0.07T or 0.030 whichever is less.That's how I read it.
Forum