welding between FSX-414 to FSX-414, (Co, Cr, Ni, Ta alloy) must be proceeding with filler metals BH/BS.
As show below:
BH: – ASME: MAR-M918
BS: – Nozzaloy (trade mark)
At this moment we don’t find this material to use during this stoppage, and we need change the filler.
Our proposal is use as filler metal: HIGHT TEMPERATURE ALLOY 617
GTAW – TIG: 61-70
AWS 5.14 - ERNiCrCoMo-1
somebody have experience in this subject? tks