Up Topic Welding Industry / Inspection & Qualification / NDT on grinded welds - Reason
- - By kar80 Date 04-28-2016 13:43
[deleted]
Parent - By Joey (***) Date 05-03-2016 02:02
Simply to ensure there are no unacceptable weld discontinuities before you put the repad. It will not be
good if there is a pinhole detected on weld under the repad during the air leak test / hydro test.
You may see this practice in a code or specification requirements.