we use TGS-2CM TIG wire and A407 welding consumable to weld P91+P22.After test,we found the C content of the area near P22 side is too low(Carbon poor). What caused the result? is it the time of PWHT too long,the dilute rate too large,and the alike? How to weld them?
Any response will be appreciated. Many thanks.