We have an ongoing problem when we EB weld 304L to Hastelloy X. In the slope out at the end of the weld fine cracks occur that show up during FPI. They appear to be quench cracks but nothing we do in changing the machine setting and speed reduces or eliminates the cracks. Does anybody have any ideas?