Hi Kix
I would not go for ERNiCu-7, because if you get too much Fe dilution you will get cracking problems. Better to stick with the Ni filler or possibly use Inconel 82. Any of the high Ni alloy fillers do not flow well, so will be a bit of a challenge if you are not use to it.
Regards
Niekie