This was from several years ago at a company that I’m no longer associated with; I've been hesitant about posting on a public forum.
The process is GMAW-P, the welds were robotically applied, the programmer had the torch push the puddle down hill. This combined with spatter build up on the end of the nozzle are what I believe was the cause.