If this is a weld surface., how are you getting rid of these fins or tears machining ,grinding, sanding, etc. What material is this.
We are finding out that different heats from the Mill will effect the shearing of our parts as well. Speeds of our press, lubricant,
strangely duller blade we get a better cut edge for weld prep surface.
Thanks