803056
I have read that to get rid of sensitized metal after welding, solution annealing is done. Heating the weldment to almost 1100 degree celcius followed by quenching, this dissociates the chromium carbide at grain boundaries and bring back chromium into the solution, reprecipitation is prevented by quenching. Hence corrosion resistance is restored. What is SAWQ you mentioned in your last post?