Sounds like you'll need some preheat, and slow cooling after welding, to prevent the cracking. St. 6 is a fairly high hardness material. If it is feasible, you could also consider switching to St. 21 which is much less crack sensitive....but also has a slightly lower hardness/wear resistance.