Application : Manufacturing of stainless steel heat exchanger.
In service equipment temperature range from 200F to 800F, with hot spot up to 1400F.
Until now we have been using stainless steel 304L.
In service problem have been very seldom.
Because of the price of 304L stainless steel we are now looking to replace it with a less expensive stainless.
We are looking at Allegheny Ludlum AL409HP, AL439HP and AL201LHP.
We know that competitors have used 409 and faced major corrosion problem, especially in the weld heat affected zone.
We wonder if AL409HP may solve the problem of weld heat affected zone corrosion.
We also wonder if 885F embrittlement may become a problem with AL439HP.
Thank you for helping me on that.
Yvan Lessard
Keep in mind this is a welding forum, and though many in here have experience with many materials in many services, I would think you would realize more success either contacting AL or perhaps posting your question at the Engineeing Tips forum. There are a lot of knowledgeable matierials guys there.
You should also check out the new Lippold/Kotecki book: Welding metallurgy and weldability of stainless steels. They have some infor on 409, but I'm not sure about the 409HP.
Not much on 409HP
Thanhs
Yvan
I've talk to John at Allegheny and got some good recommendations from him.
Thanks
Yvan Lessard
Montréal
Canada