Can anyone tell me the range of interpass temperatures that should not be exceeded when welding P91 with SMAW process? Our WPS and subsequently PQR had ranges upto 650 deg F, however we have had a resent incident where the material temperature reached 780 deg F during the welding process. Would this be deemed as detrimential to the joint integrity. Ken