Hi experts i just want to know what will be the impact temperature reductions per Table UG84.2
(1) Base material thickness is 9.27mm.
(2) Deposited weld metal thickness - GTAW (4mm) & MAW(5.27mm)
(3) MDMT temp. is -31degree Celsius.
In my opinion it will be -50 degree C. is it correct for ,multi process impact specimen?
CVN specimen for gtaw weld metal 3.3x 10mm