Recognizing that I am no steel making guy, I would say that yes, it is hot rolled. SA-941 states that hot working is deformation of a metal at temps above recrystallization. After continuous casting there is some form of hot rolling, hot deformation, or hot reduction going on, at least the applications I am aware of.