OK, I see where you're coming from. Just to make it clear, not saying that I'd do the last one, but, - for thicknesses over 3/8" and at 6G ( 4 test specimens req'd) - according to code I could do 4 side bends, or 2 face + 2 root bends, or 2 sides + 1 face + 1 root bend. I'm I correct in my interpretation. Like I said, I probably would not do the last option, just checking my thinking.
Either way it's done, the final thickness of the cross section to be bent will be 3/8"?