Did you PWHT after welding. This will often help disguise the weld on a machined surface. CA15 (410) castings need PWHT anyway due to excessive hardness in the HAZ. If you didn't PWHT, I'm surprised you aren't breaking your machining tools. I wouldn't suggets mixing and matching filler metals. ER502 is not stainless steel.